Hostalen CRP 100 RESIST CR black
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostalen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s9E4U9_Hostalen-CRP-100-RESIST-CR-black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostalen CRP 100 RESIST CR black is a high density polyethylene (HDPE), black coloured similar RAL 9004 with high melt viscosity for extrusion, injection and compression moulding. The product is classified as PE 100-RC and provides a very good long term hydrostatic strength. Especially developed for non-conventional pipe installations methods the product has a superior resistance to slow crack growth. It fulfills the material requirements of PAS 1075:2009-04 It is not intended for medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.958 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 6.4 | g/10 min | |
| 190°C/5.0 kg | 0.23 | g/10 min | |
| FNCT (80°C) 1 | > 1 | yr | ISO 16770 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Creep Modulus 2 | DIN 19537-2 | ||
| 1 min | 1.20 | GPa | |
| 2000 hr | 0.330 | GPa | |
| 24 hr | 0.560 | GPa |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (210°C) | 30 | min | ISO 11357-6 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| MRS Classification | 10.0 | MPa | ISO TR 9080 |
| Odor Threshold | < 2.00 | EN 1622/EN 1420 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 3 sec) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant (23°C) | 1100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 23.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield, 23°C | 9.0 | % | ISO 527-2/50 |
| Break | > 350 | % | EN 638 |
| Tensile Creep Modulus 3 | ISO 899-1 | ||
| 1 hr | 850 | MPa | |
| 1000 hr | 360 | MPa | |
| Flexural Stress (3.5% Strain) | 21.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 13 | kJ/m² | |
| 23°C | 26 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 74.0 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 to 280 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | 4.0 MPa, 2% Arkopal N 100 |
| 2 . | 4 point loading method |
| 3 . | 2.0 MPa load |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TARFLON™ UR2500M | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |
| Wellamid® 42L-N | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| Andur 74-AGP | Anderson Development Company | PUR-Ether/TDI | Andur |
| Axiall PVC 8150 Natural 00 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| PALFORM® R H 10 | pal plast GmbH | Acetal (POM) Homopolymer | PALFORM® |