LNP™ THERMOCOMP™ DF008 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s8cppt_LNP-THERMOCOMP-DF008-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* DF008 is a compound based on Polycarbonate resin containing 40% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound DF-1008 Product reorder name: DF008 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.52 | g/cm³ | ASTM D792 |
| -- | 1.12 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 3.0 | % | |
| Across Flow : 24 hr | 0.30 to 0.50 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.080 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.080 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 22400 | MPa | ASTM D638 |
| -- | 14400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 141 | MPa | ASTM D638 |
| Break | 132 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 6.5 | % | ASTM D638 |
| Break | 6.9 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 11600 | MPa | ASTM D790 |
| -- 5 | 11200 | MPa | ISO 178 |
| Flexural Strength 6(Break, 50.0 mm Span) | 205 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 150 | J/m | ASTM D256 |
| 23°C 7 | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 720 | J/m | ASTM D4812 |
| 23°C 8 | 45 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 138 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 141 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 134 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 140 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| New-prene™ 6185B | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| Alcryn® 2370 BK | Advanced Polymer Alloys | MPR | Alcryn® |
| Generic Vinyl Ester | Generic | Vinyl Ester | Generic |
| LUBEMID B27 GF25 NATURAL | LUBEN PLAST srl | Nylon 6 | LUBEMID |
| omay® SE21B | Suzhou OMAY Optical Materials Co., Ltd | Film, PC | omay® |