INFUSE™ 9507
| Category: | OBC , Olefin Block Copolymer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | INFUSE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s8YTA0_INFUSE-9507.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INFUSE™ 9507 Olefin Block Copolymer is a high performance olefin block copolymer that has excellent flow characteristics and performs well in a wide range of general purpose thermoplastic elastomer applications, such as injection molding and profile extrusion. INFUSE 9507 provides outstanding haptics in over molding applications with polypropylene (PP) and Polyethylene (PE). In addition its lower density can help control resin and production costs, while reducing the weight of end products. Main Characteristics:
Complies with
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.866 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, Compression Molded) | 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant (Compression Molded) | 1.49 | MPa | ASTM D638 |
| Tensile Strength (Break, Compression Molded) | 2.89 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | 1200 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 7.00 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 1900 | % | ASTM D412 |
| Tear Strength | 22.0 | kN/m | ASTM D624 |
| Compression Set | ASTM D395 | ||
| 21°C | 22 | % | |
| 70°C | 70 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 119 | °C | Internal Method |
| TMA 1(1.00 mm) | 77 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 1N, 5°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (PC) XP 610 NT | A. Schulman Europe | PC | POLYMAN® |
| RTP VLF 84707 | RTP Company | PTT | RTP |
| RTP 1005 TFE 10 | RTP Company | PBT | RTP |
| SHIN-A SE-187 | SHIN-A T&C | Epoxy | SHIN-A |
| DuPure® Y 76 | Ducor Petrochemicals BV | PP Homopolymer | DuPure® |