DOWLEX™ HMS 8017
| Category: | LLDPE , Linear Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s8MZwK_DOWLEX-HMS-8017.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DOWLEX HMS 8017 Polyethylene Resin is a Linear Low Density Polyethylene, 1-Octene Copolymer produced in Dow. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.75 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 51 µm | 168 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 176 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 10.4 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 10.6 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 49.2 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 43.2 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 630 | % | ASTM D882 |
| TD : Fracture, 51 µm | 730 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | 420 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 790 | g | ASTM D1922 |
| TD : 51 µm | 1100 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 121 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 51.0 µm) | 82 | ASTM D2457 | |
| Haze (51.0 µm) | 8.4 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Fabrication Conditions for Blown Film: Screw size: 2.3 in (60 mm); 32:1 ratio L/D Die gap: 70 mil (1.8 mm) Melt temperature 428°F (220°C) Output: 50 kg/h Die Diameter: 5.9 in (150 mm) Blow-up ratio: 2.5:1 Screw speed: 60 rpm Frost line height: 19.7 in (50 cm) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier LB02019 - C | Premier Polymers, LLC. | LLDPE | Premier |
| Baoding 67I85 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyester | Baoding |
| ExTima™ GP MB PPS 420 | Ovation Polymers Inc. | PPS | ExTima™ |
| LTP ZW-3210 | Chengdu Letian Plastics Co., Ltd | Acetal (POM) Copolymer | LTP |
| TECHNYL® A 60G1 V30 BLACK 15 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |