Infino GC-1015
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s81Wx9_Infino-GC-1015.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino GC-1015 is a Polycarbonate + ABS (PC+ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 43 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955, ISO 2577 | ||
| Flow : 3.20 mm | 0.20 to 0.30 | % | |
| Across Flow : 3.20 mm | 0.20 to 0.40 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2400 | MPa | ASTM D638 |
| -- | 2500 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 59.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Break 3 | 41.0 | MPa | ASTM D638 |
| Break | 50.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 50 | % | ASTM D638 |
| Break | 50 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2500 | MPa | ASTM D790 |
| -- 6 | 2600 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 88.0 | MPa | ASTM D790 |
| -- 8 | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 15 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 490 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 150 | J/m | ASTM D256 |
| 23°C 10 | 50 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 93.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 90.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 85.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 80.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 96.0 | °C | ISO 306/B50 |
| -- | 98.0 | °C | ISO 306/B120 |
| RTI Elec (1.50 mm) | 95.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 85.0 | °C | UL 746 |
| RTI Str (1.50 mm) | 90.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | 5VB | ||
| 2.00 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 230 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Nozzle Temperature | 260 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 93.2 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenite™ Butyrate 485E3720016 Clear, Trsp | Eastman Chemical Company | CAB | Tenite™ Butyrate |
| SUPREME HIPS SH 810 | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME HIPS |
| Moplen EP242N | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| CALP MRP440 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| SD POLYCA™ CF5301V | Sumika Styron Polycarbonate Limited | PC | SD POLYCA™ |