Badalac® ABS 30 FR
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Bada AG |
| Trademark: | Badalac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s6wc4h_Badalac-ABS-30-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Badalac® ABS 30 FR is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Europe for injection molding. Important attributes of Badalac® ABS 30 FR are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 34.0 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.95 | % | |
| Equilibrium, 23°C, 50% RH | 0.24 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2550 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 40.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 2.3 | % | ISO 527-2/50 |
| Flexural Stress (23°C) | 60.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 60 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 99.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 94.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 102 | °C | ISO 306/B50 |
| -- | 95.0 | °C | ISO 306/B120 |
| CLTE - Flow | 8.0E-5 to 1.1E-4 | cm/cm/°C | DIN 53752 |
| Maximum Service Temperature | 80 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 38 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 2.80 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 7.9E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index (1.60 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.60 mm) | 750 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 30.0 to 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Torelina® AR10M | Toray Resin Company | PPS | Torelina® |
| 4LAC® 10H23100 A-M | 4Plas | ABS | 4LAC® |
| Badamid® B70 SM-Z2 | Bada AG | Nylon 6 | Badamid® |
| Daelim Po1y® LH-4100BL | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Kumho KBR 01 | Korea Kumho Petrochemical Co., Ltd. | PBR, High Cis | Kumho KBR |