BJB Polyurethane F-62 FR A/B
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Polyurethane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s6rzA9_BJB-Polyurethane-F-62-FR-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The F-62 FR A/B system is a production oriented fire retardant system. It features a work time which allows time to vacuum de-air and cast detailed or large parts by hand, or by use of metered dispense equipment. Product Highlights:
|
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Specific Gravity | |||
| Part A | 1.21 | ||
| Part B | 1.03 | ||
| Shrinkage | 0.20 | % | ASTM D2566 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time | 10.0 | min | |
| Work Time (25°C) 1 | 6.0 - 7.0 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cure Time (25°C) | 5.0 - 7.0 | day |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 58 - 62 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 4.31 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 310 | % | ASTM D412 |
| Tear Strength | 10.5 | kN/m | ASTM D624 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 60, mixing ratio by capacity: 50 | ||
| Component B | Mixing ratio by weight: 100, mixing ratio by capacity: 100 | ||
| Shelf Life (24°C) | 26 | wk | |
| Thermoset Mix Viscosity | Brookfield | ||
| 25°C 2 | 650 | cP | Brookfield |
| 25°C 3 | 750 | cP | Brookfield |
| 25°C | 700 | cP | Brookfield |
| Demold Time (25°C) | 180 - 240 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| In order to achieve maximum physical properties, a post cure with heat is required. BJB recommends 24 hours at ambient temperature, 77°F (25°C), followed by 16 hours at 160°F (71°C). |
| Note Message | |
|---|---|
| 1 . | 100g mass |
| 2 . | Part A |
| 3 . | Part B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1960T | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| CEFOR™ 1050B | The Dow Chemical Company | LLDPE | CEFOR™ |
| Fainplast PVC GSK 78/3 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Lutene® H ME2500 | LG Chem Ltd. | HDPE | Lutene® H |
| Plaslube® PA6 CF30 TS15 BK | Techmer Engineered Solutions | Nylon 6 | Plaslube® |