Monprene® OM-10270-01
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Monprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s5rZuq_Monprene-OM-10270-01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Monprene®OM-10270-01 is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is extrusion or injection molding. Monprene®The main characteristics of the OM-10270-01 are: flame retardant/rated flame. Typical application areas include:
|
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.968 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 2.0 | g/10 min | ASTM D1238 |
| 200°C/5.0 kg | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 2.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 65 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 8.96 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 510 | % | ASTM D412 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Adhesion to ABS | |||
| Adhesion to PC | |||
| Adhesion to PC/ABS |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 138 - 160 | °C | |
| Middle Temperature | 182 - 199 | °C | |
| Front Temperature | 182 - 199 | °C | |
| Nozzle Temperature | 193 - 210 | °C | |
| Processing (Melt) Temp | 177 - 199 | °C | |
| Mold Temperature | 4.44 - 48.9 | °C | |
| Injection Pressure | 1.38 - 5.52 | MPa | |
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| 潮湿会使材料降解。建议进行干燥处理。可以把材料放入除湿干燥机，在140°F的温度下干燥2-4小时。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 138 - 149 | °C | |
| Cylinder Zone 2 Temp. | 149 - 160 | °C | |
| Cylinder Zone 3 Temp. | 160 - 182 | °C | |
| Cylinder Zone 5 Temp. | 171 - 193 | °C | |
| Die Temperature | 182 - 204 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP493M | LyondellBasell Industries | PP Homopolymer | Moplen |
| Unichem 1104-03 | Colorite Polymers | PVC, Rigid | Unichem |
| ADEKA T series | Adeka Corporation | PUR-Ether | ADEKA |
| FLEXAREN® 18020 | Innospec Leuna GmbH | EVA | FLEXAREN® |
| Kingfa PA66-C111 | Kingfa | Nylon 66 | Kingfa |