Ultradur® B 4406 G6 Q717
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultradur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s5GSGg_Ultradur-B-4406-G6-Q717.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultradur B 4406 G6 Q717 is an UL V0 injection molding, PBT grade with 30% glass fiber reinforcement. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.68 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 22.0 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.40 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % | |
| Viscosity Number (Reduced Viscosity) | 98.0 | ml/g | ISO 1628 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 11500 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.1 | % | ISO 527-2 |
| Flexural Stress (23°C) | 220 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 223 | °C | ISO 3146 |
| RTI Elec | UL 746 | ||
| 0.750 mm | 140 | °C | |
| 1.50 mm | 140 | °C | |
| 3.00 mm | 140 | °C | |
| RTI Imp | UL 746 | ||
| 0.750 mm | 130 | °C | |
| 1.50 mm | 130 | °C | |
| 3.00 mm | 130 | °C | |
| RTI Str | UL 746 | ||
| 0.750 mm | 125 | °C | |
| 1.50 mm | 130 | °C | |
| 3.00 mm | 130 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 3.90 | ||
| 1 MHz | 3.90 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 2.0E-3 | ||
| 1 MHz | 0.015 | ||
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.400 mm | V-0 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | < 1.00 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Titacon® GF915 | Titan Plastics Compounds Co., Ltd. | Acetal (POM) Copolymer | Titacon® |
| AKROMID® B3 GF 47 1 TM black (4936) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| FERREX® GPP40CA04NA | Ferro Corporation | PP Homopolymer | FERREX® |
| Huafon JF-W-HE6015 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Elvakon® 4453 | Lucite International Holland BV | Acrylic (PMMA) | Elvakon® |