UBE Nylon 1022 FDX99 Datasheet,Nylon 6,UBE Engineering Plastics, S.A.-SHANGHAI SUSHENG

Message
UBE NYLON 1022 FDX99 is a medium viscosity, nucleated Polyamide 6. The material is suitable for cast film and air-cooled blown film production.

General Information
Additive	Nucleating agent
Features	Nucleated Low smoothness Workability, good Definition, high Medium viscosity
Uses	Films
Agency Ratings	FDA Food Exposure, Not Rated European food contact, not rated
Forms	Particle
Processing Method	Blow film cast film

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.14	g/cm³	ASTM D792

Mechanical	Nominal Value	Test Method
Coefficient of Friction		ASTM D1894
With self-dynamics	1.0	ASTM D1894
With Self-Static	1.0	ASTM D1894

Films	Nominal Value	Unit	Test Method
Secant Modulus - MD (Cast Film)	650	MPa	ASTM D882
Tensile Strength - MD			ASTM D882
Yield, extruded film	32.0	MPa	ASTM D882
Fracture, extruded film	110	MPa	ASTM D882
Tensile Elongation - MD (Fracture, Extruded Film)	600	%	ASTM D882

Thermal	Nominal Value	Unit	Test Method
Melting Temperature	215	°C	DSC

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+15	ohms	ASTM D257

Optical	Nominal Value	Unit	Test Method
Gardner Gloss	155		ASTM D523
Haze	0.50	%	ASTM D1003

Additional Information
The value listed as Surface Resistivity, ASTM D257, was tested in accordance with UBE test methods.Coefficient of Friction, ASTM D1894, Dynamic: >1Coefficient of Friction, ASTM D1894, Static: >1Oxygen Permeability, ASTM D3985: 40 ml/m²/dayRelative Viscosity, JIS K6810, 96% H2SO4, conc. 1.0 g/100 ml: 3.37Extractable Content, JIS K6810: <1.00 wt%Water Vapor Permeability, JIS Z0208: 120 g/m²/dayPiercing Strength, JAS P1019, Cast Film: 9.5 NPiercing Elongation, JAS P1019, Cast Film: 14 mmFlex Crack Resistance, MIL B131B, 23°C, 1000 cycle, Cast Film: <15 hole/0.04 m²Gelbo Test, MIL B131B, 5°C, 100 cycle, Cast Film: <5 hole/0.04 m²

Additional Information

The value listed as Surface Resistivity, ASTM D257, was tested in accordance with UBE test methods.Coefficient of Friction, ASTM D1894, Dynamic: >1Coefficient of Friction, ASTM D1894, Static: >1Oxygen Permeability, ASTM D3985: 40 ml/m²/dayRelative Viscosity, JIS K6810, 96% H2SO4, conc. 1.0 g/100 ml: 3.37Extractable Content, JIS K6810: <1.00 wt%Water Vapor Permeability, JIS Z0208: 120 g/m²/dayPiercing Strength, JAS P1019, Cast Film: 9.5 NPiercing Elongation, JAS P1019, Cast Film: 14 mmFlex Crack Resistance, MIL B131B, 23°C, 1000 cycle, Cast Film: <15 hole/0.04 m²Gelbo Test, MIL B131B, 5°C, 100 cycle, Cast Film: <5 hole/0.04 m²

Category:	Nylon 6 , Polyamide 6
Manufacturer:	UBE Engineering Plastics, S.A.
Trademark:	UBE Nylon
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	s4gfy1_UBE-Nylon-1022-FDX99.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
POLYREX® PG-33	CHI MEI CORPORATION	PS (GPPS)	POLYREX®
Termaloy L-8060	Proquigel	PC+ABS	Termaloy
Borealis FR4830	Borealis AG	XLPE	Borealis
FRAGOM PR/550	Crosspolimeri S.p.A.	EVA	FRAGOM
Plaslube® ABS 7000	Techmer Engineered Solutions	ABS	Plaslube®