HAIPLEN H50 C10
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s4FIKf_HAIPLEN-H50-C10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HAIPLEN H50 C10 is a Polypropylene Homopolymer (PP Homopolymer) product filled with 50% calcium carbonate. It can be processed by injection molding and is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 0.70 | % | |
| Flow | 0.70 | % | |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 20.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 15 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 20 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 75.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 155 | °C | ISO 306/A50 |
| -- | 90.0 | °C | ISO 306/B50 |
| CLTE - Flow | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Pre-heater | 80.0 to 100 | °C | |
| Drying Time - Pre-heater | 1.0 | hr | |
| Processing (Melt) Temp | 190 to 220 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Teldene® R25MLT | National Petrochemical Industries Company (NATPET) | PP Random Copolymer | Teldene® |
| SOLARENE G153 | Dongbu Hannong Chemical | PS (GPPS) | SOLARENE |
| Ultramid® N-333 NF3001 | BASF Corporation | Nylon 66 | Ultramid® |
| Laprene® 83C000897 | SO.F.TER. SPA | SEBS | Laprene® |
| Karina IVORY COMP (SP31502) -E KAPU 6535/ 1-NT-MARFIM | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |