Honeywell PCTFE P4000LS
| Category: | PCTFE , Polychlorotrifluoroethylene |
| Manufacturer: | Honeywell |
| Trademark: | Honeywell PCTFE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s40C5O_Honeywell-PCTFE-P4000LS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Honeywell PCTFE P-Series LS film is a poly-chlor-tri-fluoroethylene homopolymer, low shrink, high performance barrier film for industrial and electronics applications. It provides outstanding water vapor barrier and excellent chemical resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.10 | g/cm³ | ASTM D792 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| MD | 1450 | MPa | ASTM D882 |
| TD | 1450 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture | 37.9 | MPa | ASTM D882 |
| TD : Fracture | 37.9 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 160 | % | ASTM D882 |
| TD : Fracture | 190 | % | ASTM D882 |
| Water Vapor Transmission | 0.047 | g/m²/24 hr | ASTM E96 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 211 | °C | ASTM D3418 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 100 | % | ASTM D2863 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | < 1.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Yield: 3267 in²/lbTensile Strength @ Break, ASTM D 882, MD: 5000 to 6000 psiTensile Strength @ Break, ASTM D 882, TD: 5000 to 6000 psiElongation @ Break, ASTM 882, MD: 110 to 200%Elongation @ Break, ASTM 882, TD: 150 to 220%Secant Modulus, ASTM D 882, MD: 190000 to 225000 psiSecant Modulus, ASTM D 882, TD: 190000 to 225000 psiGraves Tear (initial), ASTM D 1004, MD: 450 to 525 g/milGraves Tear (initial), ASTM D 1004, TD: 450 to 525 g/milDimensional Stability, ASTM D1204, TD, 300°F, 10 min: <2% shrinkageDimensional Stability, ASTM D1204, MD, 300°F, 10 min: <2% shrinkageFlammability: Non-flammable |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALLOY® B1900 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | PRIMALLOY® |
| Sylvin 9715-70 Black | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| CP PRYME® Nylon 6 N130L | Chase Plastics Services Inc. | Nylon 6 | CP PRYME® Nylon 6 |
| LNP™ LUBRICOMP™ EFL36XXC compound | SABIC Innovative Plastics | PEI | LNP™ LUBRICOMP™ |
| POLYabs SN0 | Polykemi AB | ABS | POLYabs |