RTP 2700 S-50A Z
| Category: | SEBS , Styrene Ethylene Butylene Styrene Block Copolymer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s3tsXH_RTP-2700-S-50A-Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FDA Compliant Ingredients |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.890 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 2.0 to 3.0 | % | ASTM D955 |
| Moisture Content | < 0.040 | % |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peel Strength | |||
| PP 1 | > 6.1 | kN/m | |
| PP (30% VLF) 2 | > 6.1 | kN/m | |
| PP (50% VLF) 3 | 3.2 | kN/m |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 50 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 4 | ASTM D412 | ||
| 50% Strain, 3.18 mm | 0.965 | MPa | |
| 100% Strain, 3.18 mm | 1.17 | MPa | |
| 300% Strain, 3.18 mm | 2.34 | MPa | |
| Tensile Strength 5(Break, 3.20 mm) | 6.07 | MPa | ASTM D412 |
| Tensile Elongation 6(Break) | 1100 | % | ASTM D412 |
| Tear Strength 7 | 25.4 | kN/m | ASTM D624 |
| Compression Set 8 | ASTM D395B | ||
| 23°C, 22 hr | 16 | % | |
| 70°C, 22 hr | 41 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 163 to 204 | °C | |
| Mold Temperature | 15.6 to 37.8 | °C | |
| Injection Pressure | 34.5 to 68.9 | MPa |
| Note Message | |
|---|---|
| 1 . | 90°, 20 in/min, RTP 55, Overmold Failure |
| 2 . | 90°, 20 in/min, RTP 55, Interface Failure |
| 3 . | 90°, 20 in/min, RTP 55, Interface Failure |
| 4 . | Die C |
| 5 . | Die C, 500 mm/min |
| 6 . | Die C, 500 mm/min |
| 7 . | Die C |
| 8 . | Type 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RC Plastics RCPC 8 FR | RC Plastics, Inc. (Div. of LNP Engineering Plastics) | PC | RC Plastics |
| Daelim Po1y® LL-04SJ | DAELIM INDUSTRIAL CO., LTD. | LLDPE | Daelim Po1y® |
| Infino XI-2008F | SAMSUNG SDI CO., LTD. | PPS+PPA | Infino |
| Lionpol TE-70015 | Lion Polymers Incorporated | TPE | Lionpol |
| Karina GRAY PVC COMPOUND -E800-18/258-CR-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |