LNP™ THERMOCOMP™ UX08325 compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s3UKly_LNP-THERMOCOMP-UX08325-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP THERMOCOMP UX08325 is PPA base glass fiber filled compounds, good for LDS (Laser direct structuring) application. Additional feature is high heat. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.42 | % | |
| Across Flow | 0.53 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.54 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10900 | MPa | ASTM D638 |
| -- | 11100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 135 | MPa | ASTM D638 |
| Break | 125 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.9 | % | ASTM D638 |
| Break | 1.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 9770 | MPa | ASTM D790 |
| -- 5 | 9610 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 194 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 197 | MPa | ASTM D790 |
| Break, 50.0 mm Span 7 | 195 | MPa | ASTM D790 |
| Flexural Strain at Break 8 | 2.1 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 31 | J/m | ASTM D256 |
| 23°C 9 | 2.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 350 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 264 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 262 | °C | ISO 75-2/Af |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 2.2E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 5.4E-5 | cm/cm/°C |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1.00 GHz) | 4.20 | ASTM D150 | |
| Dissipation Factor (1.00 GHz) | 0.010 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 310 to 320 | °C | |
| Middle Temperature | 315 to 325 | °C | |
| Front Temperature | 325 to 340 | °C | |
| Processing (Melt) Temp | 315 to 330 | °C | |
| Mold Temperature | 140 to 165 | °C | |
| Back Pressure | 0.200 to 0.300 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NORYL™ EFN4230 resin | SABIC Innovative Plastics Asia Pacific | PPE+PS | NORYL™ |
| Axiall PVC 1702 Clear 7070 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Devlon Acetal Homopolymer | Devol® Engineering Polymers | Acetal (POM) Homopolymer | Devlon |
| PB 910A | Pooya Polymer Tehran | Polyolefin, Unspecified | PB |
| PLANAC BT-2215-27 | TOYOBO America, Inc. | PBT | PLANAC |