Delrin® 500PE NC010
| Category: | Acetal (POM) Homopolymer , ACETAL RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Delrin® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s3GrnM_Delrin-500PE-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Medium Viscosity Acetal Homopolymer with Very Low Emissions |
| General Information | |
|---|---|
| Additive |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 14 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.9 | % | |
| Flow | 2.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | ||
| M-Scale | 93 | ||
| R-Scale | 122 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3250 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 73.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 15 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 22 | % | ISO 527-2 |
| Flexural Modulus | 3050 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 9.0 | kJ/m² | |
| 23°C | 9.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 250 | kJ/m² | |
| 23°C | 300 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 158 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 93.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 178 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.1E-4 | cm/cm/°C | |
| Flow : -40 to 23°C | 1.0E-4 | cm/cm/°C | |
| Transverse | 1.1E-4 | cm/cm/°C | |
| Transverse : -40 to 23°C | 9.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 47 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.80 | ||
| 1 MHz | 3.80 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.0E-3 | ||
| 1 MHz | 5.5E-3 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | < 2.00 | mg/kg | VDA 275 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN T-100FW | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| Sindustris ABS LHG204S | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Baytec® ME-230 (65D) | Covestro - PUR | PUR-Ether/MDI | Baytec® |
| Karina BLUE COLOR CONCENTRATE 06/213-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| CarbonResin EPU 40 | Carbon3D, Inc. | PUR, Unspecified | CarbonResin |