Stanyl® ForTii™ JTX2
| Category: | Nylon 4T , Polyamide 4T |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Stanyl® ForTii™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s1uigV_Stanyl-ForTii-JTX2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Stanyl® ForTii™ JTX2 is a Polyamide 4T (Nylon 4T) material filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America. Primary attribute of Stanyl® ForTii™ JTX2: Flame Rated. Typical application of Stanyl® ForTii™ JTX2: Electrical/Electronic Applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.41 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.3 | -- | % | |
| Flow | 0.40 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| -- | 11000 | 11000 | MPa | |
| 120°C | 8000 | -- | MPa | |
| 160°C | 4500 | -- | MPa | |
| 200°C | 4000 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| Break | 190 | 190 | MPa | |
| Break, 120°C | 135 | -- | MPa | |
| Break, 160°C | 90.0 | -- | MPa | |
| Break, 200°C | 75.0 | -- | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break | 2.2 | 2.2 | % | |
| Break, 120°C | 3.6 | -- | % | |
| Break, 160°C | 7.2 | -- | % | |
| Break, 200°C | 8.4 | -- | % | |
| Flexural Modulus | ISO 178 | |||
| -- | 10500 | -- | MPa | |
| 160°C | 5000 | -- | MPa | |
| 180°C | 4000 | -- | MPa | |
| Flexural Stress | 315 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 60 | 60 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 305 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 325 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification (0.800 mm) | HB | -- | IEC 60695-11-10, -20 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 320 to 330 | °C | |
| Middle Temperature | 325 to 335 | °C | |
| Front Temperature | 330 to 335 | °C | |
| Nozzle Temperature | 330 to 335 | °C | |
| Processing (Melt) Temp | 330 to 340 | °C | |
| Mold Temperature | 100 to 150 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.500 to 3.00 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® A VHS 338 M NER | Radici Plastics | Nylon 66 | Radilon® |
| TEKNIFLEX® VM100 | Tekni-Films, a div of Tekni-Plex | Film, PVC | TEKNIFLEX® |
| LG ABS RS800D | LG Chem Ltd. | ABS | LG ABS |
| ESTOPLAST XU 6233BL01 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |
| Sylvin 5145-75 Black 261 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |