Ronalen SV30
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Roonamid a.s. |
| Trademark: | Ronalen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s1rFaM_Ronalen-SV30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene, type reinforced with 30% chemically bounded glass fibers, natural, optimal flow properties. Suitable for injection mouldings with increased requirements to rigidity, strength and toughness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.5 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 95.0 | MPa | ISO 527-2 |
| Flexural Modulus | 5400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 163 | °C | ISO 306 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 230 to 240 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BMN P40 D | Arkema | Nylon 11 | Rilsan® |
| PTFA 25 | Polymer Tailoring Ltd. | Polyolefin, Unspecified | PTFA |
| Udel® P-3500 LCD | Solvay Specialty Polymers | PSU | Udel® |
| Multilon® TN-7000 | TEIJIN LIMITED | PC+ABS | Multilon® |
| FRAGOM PR/11 | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |