FLEXOMER™ ETS-9066 NT 7
| Category: | VLDPE , Very Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | FLEXOMER™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s1gB60_FLEXOMER-ETS-9066-NT-7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
FLEXOMER™ ETS -9066 NT 7 Very Low Density Polyethylene (VLDPE) Resin is intended for use in single or multi-layer blown-film constructions or thick sheets. Films extruded from ETS- 9066 NT 7 have a high tear strength, high impact strength, and high puncture resistance and are readily heat sealable. Addition of slip and antiblock agents should be considered for most applications.
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Puncture Energy | 4.52 | J | Internal method |
| Film Puncture Force | 53.4 | N | Internal method |
| Film Puncture Resistance | 29.8 | J/cm³ | Internal method |
| Film strength | |||
| MD | 47.2 | J/cm³ | ASTM D892 |
| TD | 59.6 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 130 | MPa | ASTM D882 |
| 2% secant, MD | 112 | MPa | ASTM D882 |
| 1% secant, TD | 129 | MPa | ASTM D882 |
| 2% secant, TD | 110 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 6.89 | MPa | ASTM D882 |
| TD : Yield | 6.21 | MPa | ASTM D882 |
| MD : Fracture | 34.1 | MPa | ASTM D882 |
| TD : Fracture | 25.8 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 330 | % | ASTM D882 |
| TD : Fracture | 560 | % | ASTM D882 |
| Dart Drop Impact | 870 | g | ASTM D1709B |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 270 | g | ASTM D1922 |
| TD | 440 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 87.8 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 99.0 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 48 | ASTM D2457 | |
| Haze | 11 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5 mm)；30:1 L/D 螺杆类型：DSBII 模具间隙：70 密尔 (1.8mm) 熔体温度：416°F (213 °C) 输出：模具周长的 10 磅/小时/英寸 模具直径：6 英寸 放大比：2.5:1 螺杆速度：59 rpm 冷冻线高度：30 分钟 (762 mm) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9726-60 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Wellamid® GFX1743-N1(PTFE) | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Hostacom CR 250 F | LyondellBasell Industries | PP, Unspecified | Hostacom |
| Rotuba CAB B9004 (13% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |
| OTECH PVC OW135 - Wire Jacket | OTECH Corporation | PVC, Unspecified | OTECH PVC |