Ultrathene® UE685009
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Ultrathene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s0ggcC_Ultrathene-UE685009.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ULTRATHENE UE 685-009 is an EVA copolymer with excellent processability and good adhesion to many substrates. Applications include extrusion coating on various substrates for flexible packaging and laminations. UE 685-009 contains no slip or antiblock. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 26 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 15.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 35 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 9.51 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 730 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 56.0 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 232 | °C |
| Extrusion instructions |
|---|
| Maximum recommended melt temperature: 450°F (232°C). |
| Note Message | |
|---|---|
| 1 . | Type 4, 510mm/min |
| 2 . | Type 4, 510mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsamid® AESN Noir T6L | Arkema | Nylon 12 | Rilsamid® |
| RTP 281 A | RTP Company | Nylon 6 | RTP |
| RTP 300 MG 20 | RTP Company | PC | RTP |
| Torelina® A670X01 | Toray Resin Company | PPS | Torelina® |
| Panlite® ML-3500ZPL | TEIJIN LIMITED | PC | Panlite® |