Adflex V 109 F
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Adflex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rzb56b_Adflex-V-109-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Adflex V 109 F is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell's proprietary Catalloy process technology. It is primarily used for molding, impact modification, extrusion coating and film applications. This resin can be used on conventional injection molding or extrusion equipment. Adflex V 109 F features a very high softness and low modulus, with a relatively high melt flow. The grade is avaiable in natural pellet form. For regulatory compliance information, see the Adflex V 109 F Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.890 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage 1(48 hr, 3.20 mm) | 0.90 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shore D, 15 sec | 30 | ASTM D2240, ISO 868 | |
| Shore A, 15 sec | 85 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 5.00 | MPa | |
| Break | 8.00 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | > 40 | % | |
| Break | > 800 | % | |
| Flexural Modulus | 80.0 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 2 | 65.0 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 2.0 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 35.0 | °C | ISO 75-2/B |
| Ductile / Brittle Transition Temperature | -55.0 | °C | ISO 6603-2 |
| Vicat Softening Temperature | 55.0 | °C | ISO 306/A50 |
| Melting Temperature | 142 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | 100x150x3.2 mm |
| 2 . | Die C, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6.6 7750 T | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| WONDERLOY® PC-345 | CHI MEI CORPORATION | PC+ABS | WONDERLOY® |
| Bayblend® T80 XG | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| Karina MBU RED E 42/404-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ RF004H compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |