FLEXITEQ™ F65A112UV
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | FLEXITEQ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ryeddw_FLEXITEQ-F65A112UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FLEXITEQ™ F65A112UV is a formulation based on Santoprene™ rubber technology. It is formulated to incorporate soft-touch, high flow and good mouldability in a pre-coloured material. FLEXITEQ™ F65A112UV is a UV improved version and can be processed on conventional thermoplastic equipment for injection moulding. It is polyolefin based and completely recyclable. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.938 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 65 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 5.30 | MPa | ASTM D412 |
| Tensile Elongation 2(Break) | 350 | % | ASTM D412 |
| Tear Strength 3(23°C) | 22.0 | kN/m | ASTM D624 |
| Compression Set 4 | ASTM D395B | ||
| 23°C, 70 hr | 27 | % | ASTM D395B |
| 70°C, 22 hr | 39 | % | ASTM D395B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 170 - 190 | °C | |
| Middle Temperature | 180 - 210 | °C | |
| Front Temperature | 190 - 210 | °C | |
| Processing (Melt) Temp | 190 - 210 | °C | |
| Mold Temperature | 10.0 - 80.0 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.300 - 0.700 | MPa | |
| Screw Speed | 100 - 200 | rpm | |
| Clamp Tonnage | 3.0 - 5.0 | kN/cm² |
| Injection instructions |
|---|
| Injection Pressure: High |
| Note Message | |
|---|---|
| 1 . | C mold, 500 mm/min |
| 2 . | Mouth die C, 500 mm/min |
| 3 . | C mold, 500 mm/min |
| 4 . | Type 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NOVADURAN® 5010CR2 | Mitsubishi Engineering-Plastics Corp | PBT | NOVADURAN® |
| Badadur® PBT8 GF30 FR | Bada AG | PBT | Badadur® |
| Celanex® 3309HRLM | Celanese Corporation | PBT | Celanex® |
| Cardia Biohybrid™ BL-F | Cardia Bioplastics™ | TPS+PE | Cardia Biohybrid™ |
| HANWHA EVA X1629 | Hanwha Chemical | EVA | HANWHA EVA |