Starflam PK0052E
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Starflam |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ryQfdo_Starflam-PK0052E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PK0052E is a Halogen Free and Red Phosphorous, Free Flame Retardant, Mineral Filled, Polyamide 6 Injection Molding (also known as PM3650Z222 or PA6 25E6 U9 Z22) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (24 hr) | 0.40 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 5100 | MPa | ISO 178 |
| Flexural Stress | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 1(23°C) | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 2(23°C) | 30 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 185 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 88.0 | °C | ISO 75-2/Af |
| Ball Pressure Test 4(125°C) | Pass | IEC 60695-10-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 450 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm, Tested by E2P) | V-2 | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 960 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 240 to 250 | °C | |
| Middle Temperature | 250 to 260 | °C | |
| Front Temperature | 250 to 270 | °C | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 125°C ±2°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNIFLEX® COC P12P | Tekni-Films, a div of Tekni-Plex | Film, PP/COC/PP | TEKNIFLEX® |
| SLOVASTER® B/E GF 30 | Plastcom | PBT | SLOVASTER® |
| Asrene® UP4806H | Chandra Asri Petrochemical | HDPE | Asrene® |
| KPOL-NYLON K-NY66/21VCF | KPOL Chem Co. | Nylon 66 | KPOL-NYLON |
| LUVOCOM® 16-8960/ES | Lehmann & Voss & Co. | PARA | LUVOCOM® |