Category: | PP, Unspecified , Polypropylene |
Manufacturer: | Vamp Tech |
Trademark: | DENILEN |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | ry188b_DENILEN-B-5010-CB.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
PP, 50% glass fiber reinforced, not Flame Retardant compound, very good mechanical properties, chemically bonded. |
General Information | |
---|---|
Filler / Reinforcement |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
Molding Shrinkage | ASTM D955 | ||
Flow | 0.20 | % | |
Across Flow | 0.50 | % | |
Water Absorption (Saturation) | 0.020 | % | ASTM D570 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Modulus | 10000 | MPa | ASTM D638 |
Tensile Strength (Yield) | 90.0 | MPa | ASTM D638 |
Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact Strength | 8.0 | kJ/m² | ISO 180/A |
Unnotched Izod Impact Strength | 35 | kJ/m² | ISO 180 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load (1.8 MPa, Unannealed) | 150 | °C | ASTM D648A |
Vicat Softening Temperature | 145 | °C | ASTM D1525 1 |
RTI Elec | 120 | °C | UL 746 |
RTI Imp | 120 | °C | UL 746 |
RTI Str | 120 | °C | UL 746 |
Injection | Nominal Value | Unit | |
---|---|---|---|
Drying Temperature | 70.0 | °C | |
Drying Time | 3.0 | hr | |
Processing (Melt) Temp | 220 | °C | |
Mold Temperature | 70.0 | °C |
Note Message | |
---|---|
1 . | Loading 2 (50 N) |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
SLOVAMID® 66 GB 30 LS | Plastcom | Nylon 66 | SLOVAMID® 66 |
Sylvin 2910-93 Green 3170 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
THERMOLAST® K TF8STE (Series: FC/CS) | KRAIBURG TPE | TPE | THERMOLAST® K |
4LOY® 10E17400 | 4Plas | PC+ABS | 4LOY® |
Karina GREEN PVC COMPOUND 550-40/107-Y | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |