LEXAN™ 135 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rxrgbi_LEXAN-135-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LEXAN 135RESIN_111 is the highest viscosity linear polycarbonate resin powder type. Suitable for extrusion processes. The product datasheet shows typical values which can be obtained when the polycarbonate powder is converted into extruded products. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 3.00 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.35 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2350 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 63.0 | MPa | |
| Break | 70.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 7.0 | % | |
| Break | 120 | % | |
| Flexural Modulus 1 | 2300 | MPa | ISO 178 |
| Flexural Stress | 90.0 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 2(1.8 MPa, Unannealed, 100 mm Span) | 128 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 144 | °C | ISO 306/B50 |
| -- | 145 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 80°C | 7.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.0E-5 | cm/cm/°C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Cylinder Zone 1 Temp. | 260 to 280 | °C | |
| Cylinder Zone 2 Temp. | 260 to 280 | °C | |
| Cylinder Zone 3 Temp. | 260 to 280 | °C | |
| Cylinder Zone 4 Temp. | 260 to 280 | °C | |
| Adapter Temperature | 260 to 280 | °C | |
| Melt Temperature | 270 to 280 | °C | |
| Die Temperature | 250 to 260 | °C | |
| Calibration Temp, First | 70.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® 94-A0907N-86NT | Teknor Apex Company | PVC, Flexible | APEX® |
| CP PRYME® Nylon 66 NN100L | Chase Plastics Services Inc. | Nylon 66 | CP PRYME® Nylon 66 |
| K-Bin Rigid PVC KB-6200 | K-Bin, Inc. | PVC, Unspecified | K-Bin Rigid PVC |
| Mafill® CR CT 5344 H | Ravago Group | PP Copolymer | Mafill® |
| SABIC® BR 4010 | Saudi Basic Industries Corporation (SABIC) | PBR, High Cis | SABIC® BR |