Celazole® (T Series) TU-60
| Category: | PBI , Polybenzimidazole |
| Manufacturer: | PBI Performance Products, Inc. |
| Trademark: | Celazole® (T Series) |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rxgbiB_Celazole-T-Series-TU-60.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celazole TU-60 is a high performance unfilled blend, ideal for applications requiring no fillers. This material works well for complex geometries and offers the best process ability. Ideal for lamp sockets, connectors and back up seals. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | |
| Water Absorption (Equilibrium) | 6.5 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (A-Scale) | 25 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5030 | MPa | ASTM D638 |
| Tensile Strength | 100 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.2 | % | ASTM D638 |
| Flexural Modulus | 5000 | MPa | ASTM D790 |
| Flexural Strength | 175 | MPa | ASTM D790 |
| Compressive Modulus | 2960 | MPa | ASTM D695 |
| Compressive Strength | 207 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | TMA | ||
| 24 to 149°C | 3.4E-5 | cm/cm/°C | TMA |
| 199 to 299°C | 7.0E-5 | cm/cm/°C | TMA |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 3.40 | ASTM D150 | |
| 10 kHz | 3.40 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 1 kHz | 0.0 | ASTM D150 | |
| 10 kHz | 1.0E-3 | ASTM D150 | |
| Arc Resistance | 135 | sec | ASTM D495 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Temperature of Intial Weight Loss | Internal method | ||
| Air | 499 | °C | Internal method |
| Nitrogen | 499 | °C | Internal method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PPR PA6603 | Premier Plastic Resins, Inc. | Nylon 66 | PPR |
| Taitacell EPS 301Ss | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| TRISTAR® PC-10R-(V6) | Polymer Technology and Services, LLC | PC | TRISTAR® |
| UNITIKA Nylon 66 E-RUNG60 | UNITIKA Plastics Division | Nylon 66 | UNITIKA Nylon 66 |
| Therma-Tech™ TT9200-5010 EC Anthracite | PolyOne Corporation | PPS | Therma-Tech™ |