DOW™ HDPE 25055E
| Category: | HDPE , High Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rx49mh_DOW-HDPE-25055E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYETHYLENE HIGH DENSITY 25055E High Density Polyethylene Resin is a very narrow molecular weight distribution resin, developed to impart excellent mechanical properties, high gloss and high surface finishing to injection moulded parts, while providing easy processing. Applications:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.955 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 25 | g/10 min | |
| 190°C/5.0 kg | 62 | g/10 min | |
| Spiral Flow | 109 | cm | Internal Method |
| Molding Shrinkage - Flow | 2.1 | % | ASTM D955 |
| Environmental Stress-Cracking Resistance (100% Antarox CO-630, Compression Molded) | 0.700 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 65 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, Compression Molded | 25.0 | MPa | |
| Break, Compression Molded | 27.0 | MPa | |
| Tensile Elongation (Break, Compression Molded) | 200 | % | ASTM D638 |
| Flexural Modulus - 2% Secant (Compression Molded) | 870 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength (Compression Molded) | 55.0 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 124 | °C | ISO 306/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Torayca® A512-X02N3 | Toray Resin Company | PPS | Torayca® |
| Evoprene™ COGEE 631 | AlphaGary | SEBS | Evoprene™ COGEE |
| Hifax EKC 107X | LyondellBasell Industries | PP Copolymer | Hifax |
| Petrothene® GA605034X02 | LyondellBasell Industries | LLDPE | Petrothene® |
| SIBUR Synthetic Rubber IR SKI-3 Group II | SIBUR | IR | SIBUR Synthetic Rubber |