PALPROP® R C 15 TV 20 Datasheet,PP Copolymer,pal plast GmbH-SHANGHAI SUSHENG

Message
PALPROP®R C 15 TV 20 is a polypropylene copolymer (PP Copoly) product, which contains 20% mineral fillers. It can be processed by injection molding and is available in Europe. PALPROP®R C 15 TV 20 applications include electrical/electronic applications and houses. Features include: anti-warping Good stiffness beautiful Impact resistance

General Information
Filler / Reinforcement	Mineral filler, 20% filler by weight
Features	Low warpage Rigid, good Impact resistance, good Excellent appearance
Uses	Electrical/Electronic Applications Shell
Appearance	Translucent
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.05	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (230°C/2.16 kg)	11.0	cm³/10min	ISO 1133
Water Absorption (Saturation, 23°C)	1.9	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	2250	MPa	ISO 527-2/1A/1
Tensile Stress (Yield, 23°C)	30.0	MPa	ISO 527-2/1A/50
Tensile Strain (Yield, 23°C)	6.5	%	ISO 527-2/1A/50
Nominal Tensile Strain at Break (23°C)	18	%	ISO 527-2/1A/50

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	3.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	45	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	92.5	°C	ISO 306/B50
Melting Temperature (DSC)	165	°C	ISO 3146

Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index (Solution A)	600	V	IEC 60112

Additional Information
Melt-Volume Flow Rate, ISO 1133, 230°C/2.16 kg: 7 to 15 cm³/10 minTensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 2000 to 2500 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 28 to 32 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 5 to 8 %Nominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: 15 to 20 %Charpy Unnotched Impact, ISO 179, Type 1, Edgewise, 23°C: 40 to 50 kJ/m²Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 2 to 4 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 90 to 95 °CDensity, ISO 1183: 1.04 to 1.06 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 1.8 to 2 %

Additional Information

Melt-Volume Flow Rate, ISO 1133, 230°C/2.16 kg: 7 to 15 cm³/10 minTensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 2000 to 2500 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 28 to 32 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 5 to 8 %Nominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: 15 to 20 %Charpy Unnotched Impact, ISO 179, Type 1, Edgewise, 23°C: 40 to 50 kJ/m²Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 2 to 4 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 90 to 95 °CDensity, ISO 1183: 1.04 to 1.06 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 1.8 to 2 %

Category:	PP Copolymer , Polypropylene Copolymer
Manufacturer:	pal plast GmbH
Trademark:	PALPROP®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	rwhB5g_PALPROP-R-C-15-TV-20.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP EMI 2560.7	RTP Company	PC+ABS	RTP
Xuchuan XCW-6032FB	Xuchuan Chemical (Suzhou) Co., Ltd	PUR, Unspecified	Xuchuan
NOVALAC RX®849	Vyncolit N.V.	Phenolic	NOVALAC
EMOPLEN® CP MTF 10	EMAS Plastik San.Tic.AS.	PP Copolymer	EMOPLEN®
Capilene® G 71 TF	Carmel Olefins Ltd.	PP Homopolymer	Capilene®