Biomer® P209
| Category: | Biodeg Polymers , Biodegradable Polymers |
| Manufacturer: | Biomer |
| Trademark: | Biomer® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rw34pG_Biomer-P209.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Properties of the resins
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Density | 1.20 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (180°C/2.16 kg) | 10 | g/10 min | |
| Melt Volume-Flow Rate (MVR) (180°C/2.16 kg) | 10.0 | cm³/10min | |
| Molding Shrinkage | 1.2 to 1.3 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.75 | % | |
| Crystallinity | 60 to 70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 4.7 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Temperature of Use | -30 to 120 | °C |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore D) | 57 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 840 to 1200 | MPa | |
| Tensile Stress 2(Yield) | 15.0 to 20.0 | MPa | |
| Tensile Strain 3(Break) | 8.0 to 15 | % | |
| Flexural Stress | |||
| 3.5% Strain | 16.0 | MPa | |
| -- | 18.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 3.4 | kJ/m² | |
| 23°C | 4.7 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 70 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 50.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 134 | °C | ISO 306/A120 |
| -- | 54.0 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | > 2.0 | hr | |
| Rear Temperature | 180 | °C | |
| Middle Temperature | 160 | °C | |
| Front Temperature | 145 to 155 | °C | |
| Nozzle Temperature | 140 | °C | |
| Processing (Melt) Temp | 195 | °C | |
| Mold Temperature | 35.0 to 55.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | > 2.0 | hr | |
| Cylinder Zone 1 Temp. | 180 | °C | |
| Cylinder Zone 2 Temp. | 160 | °C | |
| Cylinder Zone 3 Temp. | 155 | °C | |
| Cylinder Zone 4 Temp. | 145 | °C | |
| Adapter Temperature | 140 | °C | |
| Melt Temperature | > 195 | °C | |
| Die Temperature | 35.0 to 55.0 | °C |
| Note Message | |
|---|---|
| 1 . | 1 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trilliant™ HC HC6600-0010 ESD Black | PolyOne Corporation | Nylon 66 | Trilliant™ HC |
| PLUSTEK PB847I4 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |
| Polygen SG8R | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |
| Sylvin 9915-85 Blue 8364 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 8739-65FU White 1393 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |