Borealis PP ZC135
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rvh1nP_Borealis-PP-ZC135.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ZC135 is a Mineral filled polypropylene compound intended for extrusion moulding. The product is 20% Mineral filled. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 68 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield | 3.0 | % | ISO 527-2/50 |
| Fracture, 23°C | 28 | % | ISO 527-2 |
| Flexural Modulus 1 | 2700 | MPa | ISO 178 |
| Flexural Stress | 45.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 2.3 | kJ/m² | ISO 180/1A |
| 23°C | 5.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 115 | °C | ISO 75-2/Be |
| 1.8 MPa, not annealed | 66.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 96.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability (1.00 mm) | 100 | mm/min | ISO 3795 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 200 - 220 | °C | |
| Melt Temperature | 210 - 230 | °C | |
| Die Temperature | 210 - 220 | °C |
| Extrusion instructions |
|---|
| Head Temperature: 210 - 220 °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® A3W2G10 BK20560 | BASF Corporation | Nylon 66 | Ultramid® |
| Hyundai EP TOP COAT ET509B/8902 | HYUNDAI EP Co., Ltd. | PE, Unspecified | Hyundai EP TOP COAT |
| LUVOCOM® 1-3260 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Hostalen GM 5010 T3 S RED | LyondellBasell Industries | HDPE | Hostalen |
| Sylvin 9077-75 Grey 9534 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |