Plenco 01581 (Injection)
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rvbwt2_Plenco-01581-Injection-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLENCO 01581 is a glass and mineral reinforced pelletized polyester molding compound, exhibiting excellent dimensional stability, mechanical strength and also arc resistance, track resistance, and flammability ratings. UL recognized under component file E40654. 01581 is available in black and grey colors. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.83 | g/cm³ | ASTM D792 |
| Apparent Density | 0.83 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.37 | % | ASTM D6289 |
| Water Absorption (24 hr) | 0.090 | % | ASTM D570 |
| Post Shrinkage - 72 hr (120°C) | 0.010 | % | ASTM D6289 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drop Ball Impact | 267 | J/m | Internal method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Resistance | 212 | °C | ASTM D794 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 62 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11600 | MPa | ASTM D638 |
| Tensile Strength | 66.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.1 | % | ASTM D638 |
| Flexural Modulus | 10800 | MPa | ASTM D790 |
| Flexural Strength | 107 | MPa | ASTM D790 |
| Compressive Strength | 131 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 31.2 | J/m | ASTM D256 |
| Notched Izod Impact | 40 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 267 | °C | ASTM D648 |
| CLTE - Flow | 6.7E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity (100°C) | 0.91 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.7E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 14 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.40 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.021 | ASTM D150 | |
| Arc Resistance | 189 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 600 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.00 mm) | V-0 | UL 94 | |
| Oxygen Index | 47 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Shot Size | 20 - 80 | % | |
| Rear Temperature | 49.0 - 71.0 | °C | |
| Front Temperature | 85.0 - 93.0 | °C | |
| Processing (Melt) Temp | 93.0 - 100 | °C | |
| Mold Temperature | 163 - 182 | °C | |
| Injection Pressure | 6.20 - 11.0 | MPa | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm | |
| Cushion | 3.00 | mm |
| Injection instructions |
|---|
| Injection Time: 3-6 sec |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 201.3A HS | RTP Company | Nylon 6 | RTP |
| Sindustris PP HG3101 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Nylene® 406 | Custom Resins Group | Nylon 6 | Nylene® |
| Axiall PVC 8652 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Lucon® CP6067 | LG Chem Ltd. | PC | Lucon® |