TRANSMARE® 14CT40
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Transmare Compounding B.V. |
| Trademark: | TRANSMARE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rvQ4gV_TRANSMARE-14CT40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRANSMARE® 14CT40 is a copolymer polypropylene filled with 40% of mineral talc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ISO 1133 |
| Moisture Content 1 | < 0.20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 71 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield, 4.00 mm | 26.0 | MPa | ISO 527-2/50 |
| Break, 4.00 mm | 23.0 | MPa | ISO 527-2/50 |
| -- 2 | 26.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 4.00 mm) | 18 | % | ISO 527-2/50 |
| Flexural Modulus 3 | 3200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/A | ||
| -40°C | 1.3 | kJ/m² | |
| -20°C | 1.5 | kJ/m² | |
| 0°C | 2.5 | kJ/m² | |
| 23°C | 3.9 | kJ/m² |
| Note Message | |
|---|---|
| 1 . | Halogen dryer, TCR test method |
| 2 . | Maximum |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2819-80 Green 3171 | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Terluran® SP-6 | INEOS Styrolution Group GmbH | ABS | Terluran® |
| HIPOLEN P® FL 6C | HIPOL A.D. | PP Homopolymer | HIPOLEN P® |
| OmniLon™ PA6 MF30 | OMNI Plastics, LLC | Nylon 6 | OmniLon™ |
| Sylvin 8496-70FUV Black | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |