Cevian® SER90
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | PlastxWorld Inc. |
| Trademark: | Cevian® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rtTGAB_Cevian-SER90.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Cevian® SER90 is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 3.2 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 to 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 41.4 | MPa | ASTM D638 |
| Flexural Modulus (23°C) | 2070 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 68.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 92.2 | °C | ASTM D648 |
| Vicat Softening Temperature | 102 | °C | ASTM D1525 |
| CLTE - Flow | 8.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.7E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 40 | kV/mm | ASTM D149 |
| Arc Resistance (3.20 mm) | 71.0 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.57 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| 6.35 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 to 85.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 180 to 190 | °C | |
| Middle Temperature | 200 to 210 | °C | |
| Front Temperature | 220 to 230 | °C | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Pressure | 48.3 to 96.5 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.345 to 1.38 | MPa | |
| Screw Speed | 40 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1985T | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Clariant Nylon 6 PA-211G33 | Clariant Corporation | Nylon 6 | Clariant Nylon 6 |
| DESLON™ 66 DSC221M6 | DESCO Co., Ltd. | Nylon 66 | DESLON™ 66 |