| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Tenac™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rs5XYC_Tenac-GA510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tenac™ GA510 is an Acetal (POM) Homopolymer product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Tenac™ GA510 include engineering/industrial parts and housings. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 17 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow | 1.5 to 1.8 | % | |
| Across Flow | 1.2 to 1.5 | % | |
| Water Absorption (23°C, 24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 92 | ||
| R-Scale | 120 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3400 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield | 62.0 | MPa | ISO 527-2 |
| -- | 63.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 15 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 3000 | MPa | ASTM D790 |
| -- | 3200 | MPa | ISO 178 |
| Flexural Strength | 96.0 | MPa | ASTM D790 |
| Taber Abrasion Resistance | 18.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | 33 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 172 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 165 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 140 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 110 | °C | ISO 75-2/A |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM D696, ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.730 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 5186-85 White 1451 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| XENOY™ CL100 resin | SABIC Innovative Plastics Europe | PC+PBT | XENOY™ |
| Epoxies, Ect. 20-2028 | Epoxies, Etc. | PUR, Unspecified | Epoxies, Ect. |
| Hostacom TRC 411N C11547 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Durethan® BKV 135 DUS008 000000 | LANXESS GmbH | Nylon 6 | Durethan® |