ENGAGE™ 7367
| Category: | TPO (POE) , Polyolefin Elastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ENGAGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rs2vBS_ENGAGE-7367.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ENGAGE™ 7367 Polyolefin Elastomer is an ethylene-butene copolymer that has excellent flow characteristics and performs well in a wide range of general purpose thermoplastic elastomer applications This product is delivered with a nominal talc partitioning agent to assist in material handling. Main Characteristics
Applications
|
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.874 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A | 65 | ||
| Shore D | 23 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant | 2.60 | MPa | ASTM D638 |
| Tensile Strength 1(Break, Compression Molded) | 5.20 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | > 600 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant 3 | 14.1 | MPa | |
| 2% Secant | 14.2 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4 | 44.0 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | > 51.0 | °C | Internal Method |
| Vicat Softening Temperature | 42.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) 5 | 51.0 | °C | Internal Method |
| Peak Crystallization Temperature (DSC) | 13.0 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | Die C |
| 5 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G25 211 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Auracell® M | Rotuba Extruders, Inc. | CA | Auracell® |
| Hangzhou Plastic PS/PVDC/PE | Hangzhou Plastic Industry Co., Ltd. | Film, PS/PVDC/PE | Hangzhou Plastic |
| MAJ'ECO EP187L | AD majoris | PP Copolymer | MAJ'ECO |
| Sylvin 9067-65 Red 6255 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |