CALIBRE™ 351-10
| Category: | PC , Polycarbonate |
| Manufacturer: | Sumika Styron Polycarbonate Limited |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rrTPwt_CALIBRE35110.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CALIBRE™ 350 series are steam resistant grades suitable for applications used in high humid / high temperature environments such as bathroom light covers. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 - 0.70 | % | ASTM D955 |
| Transverse flow | 0.50 - 0.70 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2 |
| Tensile Strength | |||
| -- | 62.0 | MPa | ASTM D638 |
| -- | 60.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 130 | % | ASTM D638 |
| Fracture | 110 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2200 | MPa | ASTM D790 |
| -- | 2300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 89.0 | MPa | ASTM D790 |
| -- | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 75 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 890 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 140 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 135 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 126 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Lateral | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 3.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Arc Resistance | 110 | sec | ASTM D495 |
| Comparative Tracking Index | 300 | V | IEC 60112 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.585 | ASTM D542 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® MRGF30/10 42H-N | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| Baoding 67I85 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyester | Baoding |
| I. Stern N2560 | I. STERN & CO. INC. | PS (GPPS) | I. Stern |
| Petrothene® LB560210 | LyondellBasell Industries | HDPE | Petrothene® |
| OTECH PVC OE8033 - Calendering | OTECH Corporation | PVC, Unspecified | OTECH PVC |