Ghaed SAN SAN-1
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | Ghaed Basir Petrochemicals Co. |
| Trademark: | Ghaed SAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rr4R0f_Ghaed-SAN-SAN-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Classification: General grade. Characteristic: high flow Application: ABS Compounding ,ABS/PC Compounding,Cups,cosmetic container, Blower fan, pencil case, juicer, stereo dust cover&etc |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 28 to 32 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | > 81 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 23°C) | > 60.8 | MPa | ASTM D638 |
| Flexural Modulus 2(23°C) | > 3040 | MPa | ASTM D790 |
| Flexural Strength 3(23°C) | > 65.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 4 | > 2.0 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 88.0 | °C | ASTM D648 |
| Vicat Softening Temperature | > 98.0 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Rear Temperature | 190 to 200 | °C | |
| Middle Temperature | 200 to 220 | °C | |
| Front Temperature | 210 to 220 | °C | |
| Nozzle Temperature | 215 to 225 | °C | |
| Processing (Melt) Temp | 230 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Rate | Slow-Moderate |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 6.4mm |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPH 4026 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Argothane® 18212 | Argotec LLC | TPU, Unspecified | Argothane® |
| Karina GRAY PVC COMPOUND 881-18/501-E-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Golden Compound PP S²PC 2745 BO 10LP41 | Golden Compound GmbH | PP, Unspecified | Golden Compound |
| Plavis® N | Comco Nylon GmbH | PI, TP | Plavis® |