Durepol® PBT A3 G10 NTLA010 BT309 MSP
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Durepol® PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rqusze_Durepol-PBT-A3-G10-NTLA010-BT309-MSP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyester PBT reinforced with 10% fiberglass, excellent mechanical and thermal properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.70 to 1.2 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.30 | % | ASTM D570 |
| Ash Content | 7.0 to 13 | % | ASTM D2584 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 90.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.8 | % | ASTM D638 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 4000 | MPa | |
| 1000 hr | 2500 | MPa | |
| Flexural Strength | 140 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.5 | kJ/m² | ASTM D256 |
| Notched Izod Impact (Area) | 6.50 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 215 | °C | ASTM D648 |
| Vicat Softening Temperature | 215 | °C | ASTM D1525 |
| Melting Temperature | 225 | °C | ASTM D2117 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dissipation Factor | IEC 60250 | ||
| 1.00 mm, 50 Hz | 2.0E-3 | ||
| 1.00 mm, 100 Hz | 2.0E-3 | ||
| 1.00 mm, 1 MHz | 0.020 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3468 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Michilex M5000 | API Polymers, Inc. | PC | Michilex |
| Xuchuan XCS-2063B | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Braskem PP TI6550WV | Braskem America Inc. | PP Impact Copolymer | Braskem PP |
| Appeel® 20D855 | DuPont Packaging & Industrial Polymers | EA | Appeel® |