Bormed™ HD800CF
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Bormed™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rptarH_Bormed-HD800CF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bormed HD800CF is a polypropylene homopolymer. It is a film resin, suitable for the manufacturing of unoriented films on chill roll processes and blown films on tubular water quenching process. Bormed HD800CF is recommended for
Bormed HD800CF is optimised to deliver:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Molecular Weight Distribution | Medium |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Instrumented Puncture Test (50.0 µm) | 100 | J/cm | ISO 7765-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus 1(20°C, Injection Molded) | 1400 | MPa | ISO 178 |
| Coefficient of Friction 2 | > 0.70 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm | 800 | MPa | |
| TD : 50 µm | 800 | MPa | |
| Tensile Strength | ISO 527-3 | ||
| MD : 50 µm | 45.0 | MPa | |
| TD : 50 µm | 40.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm | 600 | % | |
| TD : Break, 50 µm | 650 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 164 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 50.0 µm) | > 110 | ASTM D2457 | |
| Haze (50.0 µm) | < 2.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | Film/Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2100 HF SI 2 | RTP Company | PEI | RTP |
| Megalon® 133GHSL | Mega Polymers | Nylon 66 | Megalon® |
| Badamid® LB70 K | Bada AG | Nylon 6 | Badamid® |
| DOMAMID® 66G35V0P 1001 | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| KOPA® KN126K | Kolon Plastics, Inc. | Nylon 6 | KOPA® |