Tarnamid® T- 27 GF40 FRV0
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Grupa Azoty S.A. |
| Trademark: | Tarnamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rov3ZP_Tarnamid-T--27-GF40-FRV0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% glass reinforced, heat stabilised, flame retardant, halogens and red phosphorus free. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.50 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 35.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 2.00 mm | 1.1 | -- | % | |
| Flow : 2.00 mm | 0.10 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 240 | 150 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 14000 | 8200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 165 | 105 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 4.0 | 5.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 12000 | 5800 | MPa | ISO 178 |
| Flexural Stress 2 | 240 | 135 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 8.0 | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -- | 70 | 80 | kJ/m² | |
| -30°C | 52 | -- | kJ/m² | |
| Notched Izod Impact Strength | 10 | 14 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 200 | 190 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 205 | 200 | °C | ISO 306/B |
| Melting Temperature | 221 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 1.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.0E-4 | -- | cm/cm/°C | |
| Limit of Temperature - a few hours operation | < 200 | -- | °C | |
| Temperature Index | ||||
| 20000 hr | 110 | -- | °C | |
| 5000 hr | 120 | -- | °C |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | + | -- | FMVSS 302 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA6, MFHR, 14-140, GF40 | -- | ISO 1874 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+12 | -- | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 20 | -- | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 Hz) | 4.40 | -- | IEC 60250 | |
| Dissipation Factor (1 Hz) | 0.088 | -- | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 525 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | V-0 | -- | ||
| 3.20 mm | V-0 | -- | ||
| Glow Wire Flammability Index (2.00 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Suggested Max Moisture | < 0.10 | % | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Pressure | 80.0 to 110 | MPa | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 L | RTP Company | Nylon 66 | RTP |
| Unichem E2BG-05 | Colorite Polymers | PVC, Flexible | Unichem |
| LUVOCOM® G | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| TECACOMP® PPS TRM PVX black 4008 | Ensinger GmbH | PPS | TECACOMP® |
| Sylvin 2900-80 Clear 8391 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |