LNP™ THERMOCOMP™ EC004XXC compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | roi7As_LNP-THERMOCOMP-EC004XXC-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP EC004XXC is a compound based on Polyetherimide resin containing 20% Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound EC-1004 Product reorder name: EC004XXC |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 0.10 to 0.30 | % | |
| Across Flow : 24 hr | 0.30 to 0.50 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 170 | MPa | ASTM D638 |
| Break | 175 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 12300 | MPa | ASTM D790 |
| -- | 12000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 260 | MPa | ASTM D790 |
| -- | 250 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 1 | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 530 | J/m | ASTM D4812 |
| 23°C 2 | 30 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 213 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 3 | 210 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.500 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 354 to 366 | °C | |
| Front Temperature | 366 to 377 | °C | |
| Processing (Melt) Temp | 360 to 366 | °C | |
| Mold Temperature | 121 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UNITAL® C BK | Nytef Plastics, Ltd. | Acetal (POM) Copolymer | UNITAL® |
| Nipol® 1571H | Zeon Corporation | Latex | Nipol® |
| Hylon® N1033L | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Lionpol IM-40046 | Lion Polymers Incorporated | TPE | Lionpol |
| ESTOPLAST ZK 6002GY32 | Ester Industries Ltd. | PC | ESTOPLAST ZK |