SUPREME Specialty PS SP556
| Category: | PS (IRPS) , Ignition Resistant Polystyrene |
| Manufacturer: | Supreme Petrochem Ltd. |
| Trademark: | SUPREME Specialty PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rnih3g_SUPREME-Specialty-PS-SP556.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Flame Retardant Polystyrene (FR-HIPS) Characteristics:
Processing:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 4.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(23°C, 3.20 mm, Injection Molded) | 28.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, 3.20 mm, Injection Molded) | 30 | % | ASTM D638 |
| Flexural Modulus (23°C, 3.20 mm, Injection Molded) | 1800 | MPa | ASTM D790 |
| Flexural Strength (23°C, 3.20 mm, Injection Molded) | 38.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, Injection Molded) | 81.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 103 | °C | ASTM D1525 3 |
| Ball Indentation Temperature | 82.0 | °C | IEC 60598-1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity (3.20 mm) | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity (3.20 mm) | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Constant (23°C, 3.20 mm, 1 MHz) | 2.60 | IEC 60250 | |
| Dissipation Factor (23°C, 3.20 mm, 1 MHz) | 4.0E-4 | IEC 60250 | |
| Comparative Tracking Index (3.20 mm) | 450 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 960 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| Surface Resistivity, IEC 60093, 23°C, 3.2mm: >1E14 ohmsVolume Resistivity, IEC 60093, 23°C, 3.2mm: >1E16 ohm-cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 250 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Melt Temperature | 250 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 标准 B (120°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefabloc® TP SD 300 50A | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| TRIREX® Compound NH3025NT | Samyang Corporation | PC | TRIREX® Compound |
| Bynel® 41E755 | DuPont Packaging & Industrial Polymers | LLDPE | Bynel® |
| Ebalta GM 959 / GM 959-1 | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| Deltron 1150 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PPS | Deltron |