Clearflex® H&T FGH B3
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Clearflex® H&T |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rltGkc_ClearflexHampTFGHB3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clearflex H&T FGH B3 is a linear low density polyethylene, made by proprietary enhanced Z-N catalyst, suitable for blown film technology. The resin, containing antioxidants slip agent and antiblock, is characterized by a very low density and high molecular weight. Compared to std Clearflex VLDPE grades, Clearflex H&T FGH B3 offers lower seal initiation temperature, excellent optical properties and mechanical performances. Main Applications Clearflex H&T FGH B3 is recommended to produce blown film requiring a combination of optical properties, puncture resistance and impact strength and very good sealability. Clearflex H&T FGH B3 is also recommended in the production of Lamination film. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.911 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 10 to 50 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% sectioning, MD : Blown film | 140 | MPa | ISO 527-3 |
| 1% sectioning, TD : Blown film | 135 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : yield, blow film | 5.00 | MPa | ISO 527-3 |
| TD : yield, blow film | 6.00 | MPa | ISO 527-3 |
| MD : fracture, blow film | 31.0 | MPa | ISO 527-3 |
| TD : fracture, blow film | 29.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : fracture, blow film | 460 | % | ISO 527-3 |
| TD : fracture, blow film | 660 | % | ISO 527-3 |
| Dart Drop Impact (Blown Film) | 270 | g | ISO 7765-1/A |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD | 75.0 | kN/m | ISO 6383-2 |
| TD | 115.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 85.0 | °C | ISO 306/A |
| Melting Temperature | 110 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, Blown Film) | 72 | ASTM D2457 | |
| Haze (Blown Film) | 4.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 - 230 | °C |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 TFE 13 SI 2 | RTP Company | Nylon 66 | RTP |
| Rely-imide 613 | Henkel Ablestik | TP, Unspecified | Rely-imide |
| apilon 52® 7013 | API SpA | TPU-Polyester | apilon 52® |
| Loyblend® TA-1100 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PC+ABS | Loyblend® |
| Petro Rabigh PE B2555 | Rabigh Refining & Petrochemical Co. | HDPE | Petro Rabigh PE |