BLUESTAR® PBT 403G-M30
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Nantong Zhonglan Engineering Plastics Co., Ltd. |
| Trademark: | BLUESTAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rlXIRC_BLUESTAR-PBT-403G-M30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BLUESTAR® PBT 403G-M30 is a Polybutylene Terephthalate (PBT) product filled with 30% mineral. It is available in Asia Pacific or North America. Typical application: Electrical/Electronic Applications. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.62 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 19 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 | % | |
| Across Flow | 0.60 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.16 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9000 | MPa | ASTM D638 |
| Tensile Strength (Break) | 110 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 8000 | MPa | ASTM D790 |
| Flexural Strength | 175 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Area) (23°C) | 11.0 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact (Area) (23°C) | 65.0 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 220 | °C | |
| 1.8 MPa, Unannealed | 207 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.3E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-0 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Ignition Temperature | 750 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® B3WG5 BK00564 | BASF Corporation | Nylon 6 | Ultramid® |
| Multiuse Leostomer® LE-3140N | Riken Technos Corp. | TPU, Unspecified | Multiuse Leostomer® |
| EVALENE® PP PHJ1201 | JG Summit Petrochemical Corporation | PP Homopolymer | EVALENE® PP |
| DOW™ Electrical & Telecommunications DGDA-1310 NT | The Dow Chemical Company | HDPE | DOW™ Electrical & Telecommunications |
| Sylvin 8200-80UV Clear 8418 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |