POLYfill PPH TS5040
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYfill |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rlEFGc_POLYfill-PPH-TS5040.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Mineral reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.90 to 1.1 | % | |
| Flow | 0.90 to 1.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 28.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 3200 | MPa | ISO 178 |
| Flexural Stress | 54.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 2.0 | kJ/m² | |
| 23°C | 3.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 122 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 146 | °C | ISO 306/A50 |
| -- | 84.0 | °C | ISO 306/B50 |
| CLTE - Flow | 5.0E-5 to 7.5E-5 | cm/cm/°C | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROBLEND 85 X0 | Taro Plast S.p.A. | PC+ABS | TAROBLEND |
| Tuffak® T | Altuglas International of Arkema Inc. | PC | Tuffak® |
| Globalene® PI0106 | Lee Chang Yung Chemical Industry Corp. | PP Alloy | Globalene® |
| KOPLA PA66 KDX1067 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| Durethan® BKV 215 H2.0 901510 | LANXESS GmbH | Nylon Copolymer | Durethan® |