VAMPSON L 3010
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Vamp Tech |
| Trademark: | VAMPSON |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rknALi_VAMPSON-L-3010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Linear PPS, 30% glass fiber reinforced, UL 94 V0 at 3,2 mm, halogen and red phosphorus free, high chemical resistance and excellent operating temperature, good mechanicals properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.58 | g/cm³ | ASTM D792 |
| Water Absorption (Saturation) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12000 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 150 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.9 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 6.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 30 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 255 | °C | ASTM D648A |
| Vicat Softening Temperature | 250 | °C | ASTM D1525 1 |
| RTI Elec | 200 | °C | UL 746 |
| RTI Imp | 200 | °C | UL 746 |
| RTI Str | 200 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 320 | °C | |
| Mold Temperature | 140 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Surlyn® 1605 | DuPont Packaging & Industrial Polymers | Ionomer | Surlyn® |
| Mowiol® 6-98 | Kuraray Co., Ltd. | PVOH | Mowiol® |
| Eastman™ 1223 | Eastman Chemical Company | Copolyester | Eastman™ |
| Laprene® 8K1000A90 | SO.F.TER. SPA | SEBS | Laprene® |
| INSULCAST® MRTV 2 | ITW Polymers Coatings North America | Silicone Rubber, RTV-2 | INSULCAST® |