Generic Nylon, Unspecified - Glass Fiber
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rkfryb_Generic-Nylon-Unspecified---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon, Unspecified - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 - 1.65 | g/cm³ | ASTM D792 |
| 23°C | 1.37 - 1.72 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.10 - 0.53 | % | ASTM D955 |
| 23°C | 3.0E-3 - 1.1 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.15 - 0.53 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 122 - 125 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 3330 - 14700 | MPa | ASTM D638 |
| 23°C | 3300 - 24800 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 27.0 - 260 | MPa | ASTM D638 |
| Fracture, 23°C | 26.0 - 260 | MPa | ASTM D638 |
| Fracture, 23°C | 56.0 - 260 | MPa | ISO 527-2 |
| 23°C | 119 - 235 | MPa | ASTM D638 |
| 23°C | 169 - 247 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 1.5 - 5.0 | % | ASTM D638 |
| Fracture, 23°C | 2.0 - 4.6 | % | ASTM D638 |
| Fracture, 23°C | 1.7 - 2.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2570 - 15400 | MPa | ASTM D790 |
| 23°C | 6420 - 19000 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 158 - 349 | MPa | ASTM D790 |
| 23°C | 86.0 - 417 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 - 17 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 35 - 96 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 37 - 140 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 240 - 1300 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 138 - 224 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 254 - 262 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 139 - 288 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 224 - 270 | °C | ISO 75-2/A |
| Melting Temperature | 220 - 266 | °C | ISO 11357-3 |
| CLTE - Flow | 2.2E-5 - 4.4E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 - 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+4 - 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 19 - 24 | kV/mm | ASTM D149 |
| Comparative Tracking Index | 593 - 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 78.4 - 82.9 | °C | |
| Drying Time | 3.9 - 4.1 | hr | |
| Dew Point | -40.0 - -39.4 | °C | |
| Suggested Max Moisture | 0.10 - 0.20 | % | |
| Rear Temperature | 259 - 330 | °C | |
| Middle Temperature | 285 - 330 | °C | |
| Front Temperature | 269 - 330 | °C | |
| Processing (Melt) Temp | 280 - 328 | °C | |
| Mold Temperature | 80.0 - 149 | °C | |
| Injection Pressure | 84.6 - 115 | MPa | |
| Back Pressure | 0.255 - 0.436 | MPa | |
| Screw Speed | 45 - 70 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon, Unspecified - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 6 GF 35 FRC 5 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| Nanjing Hongrui PP P1304 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PP, Unspecified | Nanjing Hongrui PP |
| Addisil™ 160 E | Momentive Performance Materials Inc. | Rubber | Addisil™ |
| MAJORIS CETAL DN010 | AD majoris | Acetal (POM) Copolymer | MAJORIS |
| SQUARE® LSG1001-09A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |