Eltex® PF6012KJ

Category:	mLLDPE , Metallocene Linear Low Density Polyethylene
Manufacturer:	INEOS Olefins & Polymers Europe
Trademark:	Eltex®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	rk89EK_EltexPF6012KJ.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Eltex® PF6012KJ is a metallocene LLDPE resin produced in Europe.

Applications
Eltex® PF6012KJ has been developed for use in highly technical film like food packaging, lamination, and other thin film applications where superior mechanical and sealing performance is required. In addition, Eltex® PF6012KJ offers easy extrudability and distinctive sealing properties.

Benefits and Features
Eltex® PF6012KJ is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. It offers the following properties:

Outstanding impact strength

Low blocking for the film together with low abrasive character for the extrusion equipment

Very low sealing initiation temperature

Excellent Hot Tack strength, particularly advantageous for HFFS packaging lines

Very good bubble stability and extrudability similar to best LLDPE blown film grade

Properties ideally balanced in machine and transverse directions

Eltex® PF6012KJ is formulated with slip and antiblocking agents that offer high slip with easy opening properties. Addition of other polymers, masterbatches and pigments may alter film slip and antiblock performance.

General Information
Additive	Erucamide Lubricating Additive (1000 ppm) Anti-caking agent (300 ppm) 2 Antioxidation
Features	Low density Low temperature heat sealability High smoothness Copolymer hexene comonomer Anti-caking property Antioxidation Impact resistance, high Workability, good Compliance of Food Exposure
Uses	Films Laminate Food packaging
RoHS Compliance	Contact manufacturer
Forms	Particle
Processing Method	Lamination method Extrusion

Physical	Nominal Value	Unit	Test Method
Density (23°C)	0.913	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.3	g/10 min	ISO 1133

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	25	µm
Tensile Modulus			ISO 527-3
1% secant, MD : 25 µm, blown film	140	MPa	ISO 527-3
1% secant, TD : 25 µm, blown film	140	MPa	ISO 527-3
Tensile Stress			ISO 527-3
MD : Yield, 25 µm, blown film	8.00	MPa	ISO 527-3
TD : Yield, 25 µm, blown film	8.00	MPa	ISO 527-3
MD : Broken, 25 µm, blown film	65.0	MPa	ISO 527-3
TD : Broken, 25 µm, blown film	64.0	MPa	ISO 527-3
Tensile Elongation			ISO 527-3
MD : Broken, 25 µm, blown film	480	%	ISO 527-3
TD : Broken, 25 µm, blown film	610	%	ISO 527-3
Dart Drop Impact (25 µm, Blown Film)	> 1600	g	ASTM D1709A
Elmendorf Tear Strength			ASTM D1922
MD : 25 µm, blown film	180	g	ASTM D1922
TD : 25 µm, blown film	360	g	ASTM D1922

Thermal	Nominal Value	Unit	Test Method
Melting Temperature (DSC)	97.0 - 114	°C	Internal method

Optical	Nominal Value	Unit	Test Method
Gloss (45°, 25.0 µm, Blown Film)	79		ASTM D2457
Haze (25.0 µm, Blown Film)	4.0	%	ASTM D1003

Extrusion	Nominal Value	Unit
Melt Temperature	190 - 230	°C

Resin Grade	Manufacturer	Category	Trademark
PROTEQ™ C35UST2	Marplex Australia Pty. Ltd.	PP Copolymer	PROTEQ™
RheTech Polypropylene HP532-01	RheTech, Inc.	PP, Unspecified	RheTech Polypropylene
Varcum 94607	Durez Corporation	Phenolic	Varcum
Nypol® PA A3 FR NTLA010 NR309	Petropol Industry and Trade of Polymers LTDA	Nylon 66	Nypol® PA
ColorFast® FRPBT200	LTL Color Compounders, Inc.	PBT	ColorFast®