KOPLA PA66 KDE1020
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | KOPLA Co., Ltd. |
| Trademark: | KOPLA PA66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | riXlFr_KOPLA-PA66-KDE1020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KOPLA PA66 KDE1020 is a Polyamide 66 (Nylon 66) material. It is available in Asia Pacific. Important attributes of KOPLA PA66 KDE1020 are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.9 to 3.0 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.2 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 49.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 80 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1770 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 64.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 200 | °C | |
| 1.8 MPa, Unannealed | 63.0 | °C | |
| Melting Temperature | 260 | °C | |
| CLTE - Flow | 7.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 24 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.20 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.020 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® S 24E 100 NAT | Radici Plastics | Nylon 6 | Radilon® |
| Talcoprene® 520TL LE NERO | SO.F.TER. SPA | PP Homopolymer | Talcoprene® |
| Zythane® 8080DU | Alliance Polymers & Services | TPU-Polyether | Zythane® |
| E-FLEX™ S4060 | Mando Advanced Materials Co., Ltd. | TPE | E-FLEX™ |
| Plasmer 1065BM/8901 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |