PLUSTEK PB202G50BK39
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | PLUSTEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | riG56t_PLUSTEK-PB202G50BK39.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 50% GLASS FIBER REINFORCED, UV AND HEAT SATBILIZED POLYAMIDE 6 . APPROVED AND LISTED BY NSF/ANSI 61 INTERNATIONAL. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.10 to 0.40 | % | ASTM D955 |
| -- | 0.10 to 0.40 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 4.8 | % | ASTM D570 |
| Saturation, 23°C | 4.8 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.5 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13000 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 210 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 13700 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 305 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 200 | J/m | ASTM D256 |
| 23°C | 19 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 220 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature | |||
| -- | 110 | °C | |
| -- 1 | 200 | °C | |
| Melting Temperature | 218 | °C | ISO 11357-3, ASTM D3417 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 80 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.80 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | SHORT PEAKS OPERATION |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wondel® B BN0F | Nanjing Julong Engineering Plastics Co., LTD | Nylon 6 | Wondel® B |
| ACCUCOMP™ ABS811L | ACLO Compounders Inc. | ABS | ACCUCOMP™ |
| ALCUDIA® HDPE M5204 | REPSOL | HDPE | ALCUDIA® HDPE |
| Flexathene® PD907 | LyondellBasell Industries | Polyolefin, Unspecified | Flexathene® |
| ELASTOSIL® R 805/75 | Wacker Chemie AG | Silicone | ELASTOSIL® R |