ISPLEN® PM 750 AS
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | REPSOL |
| Trademark: | ISPLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rhaf6r_ISPLEN-PM-750-AS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene homopolymer, 55% mineral fillers reinforced and low melt flow rate. ISPLEN® PM 750 AS shows a high stiffness, as well as a low warpage and shrinkage behaviour. This product is standard stabilised, able to be used in the main applications. APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | 0.43 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 75 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6650 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 24.0 | MPa | |
| Break | 30.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 0.40 | % | |
| Break | 1.1 | % | |
| Flexural Modulus | 7300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 1.0 | kJ/m² | |
| -20°C | 1.0 | kJ/m² | |
| 0°C | 1.0 | kJ/m² | |
| 23°C | 1.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -40°C | 5.5 | kJ/m² | |
| -20°C | 5.5 | kJ/m² | |
| 0°C | 5.5 | kJ/m² | |
| 23°C | 7.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 135 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 97.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 158 | °C | ISO 306/A120 |
| -- | 109 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 150x100x3mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax PI674 | INDELPRO, S.A. de C.V. | PP Homopolymer | Pro-fax |
| Durethan® AKV 30 HR H2.0 900116 | LANXESS GmbH | Nylon 66 | Durethan® |
| LNP™ STAT-KON™ EX02598C compound | SABIC Innovative Plastics | PEI | LNP™ STAT-KON™ |
| Hifax BC 72 A/1 3001 | LyondellBasell Industries | PP Copolymer | Hifax |
| Edistir® N 3982 | Versalis S.p.A. | PS (GPPS) | Edistir® |